SAE-AISI P21 Steel vs. N06002 Nickel

SAE-AISI P21 steel belongs to the iron alloys classification, while N06002 nickel belongs to the nickel alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI P21 steel and the bottom bar is N06002 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 1130
760

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Melting Completion (Liquidus), °C 1450
1360
Melting Onset (Solidus), °C 1410
1260
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 41
9.9
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
55
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 2.3
9.3
Embodied Energy, MJ/kg 32
130
Embodied Water, L/kg 62
270

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 40
25
Strength to Weight: Bending, points 31
22
Thermal Diffusivity, mm2/s 11
2.6
Thermal Shock Resistance, points 37
19

Alloy Composition

Carbon (C), % 0.18 to 0.22
0.050 to 0.15
Chromium (Cr), % 0 to 0.5
20.5 to 23
Cobalt (Co), % 1.1 to 1.3
0.5 to 2.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 92.1 to 94.2
17 to 20
Manganese (Mn), % 0.35 to 0.72
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 3.9 to 4.3
42.3 to 54
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
0.2 to 1.0
Vanadium (V), % 0.15 to 0.25
0