SAE-AISI P21 Steel vs. S82122 Stainless Steel

Both SAE-AISI P21 steel and S82122 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI P21 steel and the bottom bar is S82122 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Rockwell C Hardness 35
28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 1130
680

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
15
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
12
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 2.3
2.6
Embodied Energy, MJ/kg 32
37
Embodied Water, L/kg 62
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 40
25
Strength to Weight: Bending, points 31
22
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 37
19

Alloy Composition

Carbon (C), % 0.18 to 0.22
0 to 0.030
Chromium (Cr), % 0 to 0.5
20.5 to 21.5
Cobalt (Co), % 1.1 to 1.3
0
Copper (Cu), % 0 to 0.25
0.5 to 1.5
Iron (Fe), % 92.1 to 94.2
68.9 to 75.4
Manganese (Mn), % 0.35 to 0.72
2.0 to 4.0
Molybdenum (Mo), % 0
0 to 0.6
Nickel (Ni), % 3.9 to 4.3
1.5 to 2.5
Nitrogen (N), % 0
0.15 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0.15 to 0.25
0