SAE-AISI P5 Steel vs. EN 2.4663 Nickel

SAE-AISI P5 steel belongs to the iron alloys classification, while EN 2.4663 nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI P5 steel and the bottom bar is EN 2.4663 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 370 to 1980
780

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 45
13
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
75
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.5
11
Embodied Energy, MJ/kg 20
140
Embodied Water, L/kg 56
350

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 13 to 70
25
Strength to Weight: Bending, points 15 to 45
22
Thermal Diffusivity, mm2/s 12
3.5
Thermal Shock Resistance, points 12 to 65
22

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.4
Boron (B), % 0
0 to 0.0060
Carbon (C), % 0 to 0.1
0.050 to 0.1
Chromium (Cr), % 2.0 to 2.5
20 to 23
Cobalt (Co), % 0
11 to 14
Copper (Cu), % 0 to 0.25
0 to 0.5
Iron (Fe), % 95.7 to 97.8
0 to 2.0
Manganese (Mn), % 0.2 to 0.6
0 to 0.2
Molybdenum (Mo), % 0
8.5 to 10
Nickel (Ni), % 0 to 0.35
48 to 59.6
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 0.4
0 to 0.2
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.2 to 0.6