SAE-AISI S4 Steel vs. EN 1.4869 Casting Alloy
SAE-AISI S4 steel belongs to the iron alloys classification, while EN 1.4869 casting alloy belongs to the nickel alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI S4 steel and the bottom bar is EN 1.4869 casting alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 2140 | |
| 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 330 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1450 |
| Melting Onset (Solidus), °C | 1390 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Conductivity, W/m-K | 44 | |
| 10 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 70 |
| Density, g/cm3 | 7.7 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 7.7 |
| Embodied Energy, MJ/kg | 29 | |
| 110 |
| Embodied Water, L/kg | 48 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 77 | |
| 18 |
| Strength to Weight: Bending, points | 22 to 48 | |
| 17 |
| Thermal Diffusivity, mm2/s | 12 | |
| 2.6 |
| Thermal Shock Resistance, points | 20 to 65 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0.5 to 0.65 | |
| 0.45 to 0.55 |
| Chromium (Cr), % | 0.1 to 0.5 | |
| 24 to 26 |
| Cobalt (Co), % | 0 | |
| 14 to 16 |
| Iron (Fe), % | 95.2 to 96.9 | |
| 11.4 to 23.6 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 33 to 37 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 1.8 to 2.3 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 4.0 to 6.0 |
| Vanadium (V), % | 0.15 to 0.35 | |
| 0 |