SAE-AISI S5 Steel vs. SAE-AISI F1 Steel
Both SAE-AISI S5 steel and SAE-AISI F1 steel are iron alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI S5 steel and the bottom bar is SAE-AISI F1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 1940 | |
| 620 to 2320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1480 |
| Melting Onset (Solidus), °C | 1400 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 42 | |
| 45 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.1 | |
| 5.0 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.1 | |
| 1.7 |
| Embodied Energy, MJ/kg | 29 | |
| 24 |
| Embodied Water, L/kg | 51 | |
| 46 |
Common Calculations
| PREN (Pitting Resistance) | 2.9 | |
| 2.3 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 25 to 70 | |
| 22 to 82 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 20 to 49 |
| Thermal Diffusivity, mm2/s | 11 | |
| 12 |
| Thermal Shock Resistance, points | 23 to 65 | |
| 19 to 70 |
Alloy Composition
| Carbon (C), % | 0.5 to 0.65 | |
| 1.0 to 1.3 |
| Chromium (Cr), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 93.6 to 97 | |
| 95.9 to 98 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.2 to 1.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 1.8 to 2.3 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 1.0 to 1.8 |
| Vanadium (V), % | 0 to 0.35 | |
| 0 |