SAE-AISI T15 Steel vs. EN 1.4864 Stainless Steel

Both SAE-AISI T15 steel and EN 1.4864 stainless steel are iron alloys. They have 52% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI T15 steel and the bottom bar is EN 1.4864 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 76
75
Tensile Strength: Ultimate (UTS), MPa 830 to 2240
650

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1690
1390
Melting Onset (Solidus), °C 1640
1340
Specific Heat Capacity, J/kg-K 430
480
Thermal Conductivity, W/m-K 21
13
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 43
30
Density, g/cm3 8.7
8.0
Embodied Carbon, kg CO2/kg material 16
5.3
Embodied Energy, MJ/kg 250
75
Embodied Water, L/kg 140
180

Common Calculations

PREN (Pitting Resistance) 27
17
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 26 to 71
23
Strength to Weight: Bending, points 22 to 43
21
Thermal Diffusivity, mm2/s 5.6
3.3
Thermal Shock Resistance, points 26 to 70
17

Alloy Composition

Carbon (C), % 1.5 to 1.6
0 to 0.15
Chromium (Cr), % 3.8 to 5.0
15 to 17
Cobalt (Co), % 4.8 to 5.3
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 67.5 to 73.5
41.7 to 51
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 0 to 0.3
33 to 37
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.15 to 0.4
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 11.8 to 13
0
Vanadium (V), % 4.5 to 5.3
0