SAE-AISI T15 Steel vs. SAE-AISI M36 Steel
Both SAE-AISI T15 steel and SAE-AISI M36 steel are iron alloys. They have 90% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI T15 steel and the bottom bar is SAE-AISI M36 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 2240 | |
| 810 to 2190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1690 | |
| 1600 |
| Melting Onset (Solidus), °C | 1640 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 440 |
| Thermal Conductivity, W/m-K | 21 | |
| 19 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 43 | |
| 38 |
| Density, g/cm3 | 8.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 16 | |
| 9.5 |
| Embodied Energy, MJ/kg | 250 | |
| 140 |
| Embodied Water, L/kg | 140 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 27 | |
| 31 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 |
| Strength to Weight: Axial, points | 26 to 71 | |
| 27 to 72 |
| Strength to Weight: Bending, points | 22 to 43 | |
| 23 to 44 |
| Thermal Diffusivity, mm2/s | 5.6 | |
| 5.1 |
| Thermal Shock Resistance, points | 26 to 70 | |
| 25 to 68 |
Alloy Composition
| Carbon (C), % | 1.5 to 1.6 | |
| 0.8 to 0.9 |
| Chromium (Cr), % | 3.8 to 5.0 | |
| 3.8 to 4.5 |
| Cobalt (Co), % | 4.8 to 5.3 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 67.5 to 73.5 | |
| 70.1 to 75.5 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 4.6 to 5.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0.2 to 0.45 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 11.8 to 13 | |
| 5.5 to 6.5 |
| Vanadium (V), % | 4.5 to 5.3 | |
| 1.8 to 2.3 |