SAE-AISI T2 Steel vs. Grade 19 Titanium
SAE-AISI T2 steel belongs to the iron alloys classification, while grade 19 titanium belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI T2 steel and the bottom bar is grade 19 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 79 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 2150 | |
| 890 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 400 |
| Melting Completion (Liquidus), °C | 1820 | |
| 1660 |
| Melting Onset (Solidus), °C | 1760 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 520 |
| Thermal Conductivity, W/m-K | 19 | |
| 6.2 |
| Thermal Expansion, µm/m-K | 12 | |
| 9.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 46 | |
| 45 |
| Density, g/cm3 | 9.3 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 47 |
| Embodied Energy, MJ/kg | 170 | |
| 760 |
| Embodied Water, L/kg | 98 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 33 |
| Strength to Weight: Axial, points | 23 to 64 | |
| 49 to 72 |
| Strength to Weight: Bending, points | 20 to 40 | |
| 41 to 53 |
| Thermal Diffusivity, mm2/s | 4.9 | |
| 2.4 |
| Thermal Shock Resistance, points | 23 to 65 | |
| 57 to 83 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0.8 to 0.9 | |
| 0 to 0.050 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 5.5 to 6.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 70.8 to 75.8 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 71.1 to 77 |
| Tungsten (W), % | 17.5 to 19 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.4 | |
| 7.5 to 8.5 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |