SAE-AISI T4 Steel vs. N08031 Stainless Steel
Both SAE-AISI T4 steel and N08031 stainless steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI T4 steel and the bottom bar is N08031 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 2140 | |
| 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Melting Completion (Liquidus), °C | 1810 | |
| 1440 |
| Melting Onset (Solidus), °C | 1750 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 460 |
| Thermal Conductivity, W/m-K | 21 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 39 |
| Density, g/cm3 | 9.4 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 7.1 |
| Embodied Energy, MJ/kg | 130 | |
| 96 |
| Embodied Water, L/kg | 120 | |
| 240 |
Common Calculations
| PREN (Pitting Resistance) | 37 | |
| 52 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 64 | |
| 25 |
| Strength to Weight: Bending, points | 20 to 39 | |
| 22 |
| Thermal Diffusivity, mm2/s | 5.4 | |
| 3.1 |
| Thermal Shock Resistance, points | 24 to 64 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0.7 to 0.8 | |
| 0 to 0.015 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 26 to 28 |
| Cobalt (Co), % | 4.3 to 5.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 1.0 to 1.4 |
| Iron (Fe), % | 66.3 to 72.3 | |
| 29 to 36.9 |
| Manganese (Mn), % | 0.1 to 0.4 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.4 to 1.0 | |
| 6.0 to 7.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 30 to 32 |
| Nitrogen (N), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Tungsten (W), % | 17.5 to 19 | |
| 0 |
| Vanadium (V), % | 0.8 to 1.2 | |
| 0 |