SAE-AISI T5 Steel vs. AISI 304Cu Stainless Steel
Both SAE-AISI T5 steel and AISI 304Cu stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI T5 steel and the bottom bar is AISI 304Cu stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 860 to 2140 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Melting Completion (Liquidus), °C | 1810 | |
| 1410 |
| Melting Onset (Solidus), °C | 1750 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 480 |
| Thermal Conductivity, W/m-K | 21 | |
| 13 |
| Thermal Expansion, µm/m-K | 11 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 16 |
| Density, g/cm3 | 9.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 3.0 |
| Embodied Energy, MJ/kg | 170 | |
| 43 |
| Embodied Water, L/kg | 140 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 37 | |
| 18 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 25 to 63 | |
| 19 |
| Strength to Weight: Bending, points | 21 to 39 | |
| 19 |
| Thermal Diffusivity, mm2/s | 5.5 | |
| 3.5 |
| Thermal Shock Resistance, points | 26 to 66 | |
| 12 |
Alloy Composition
| Carbon (C), % | 0.75 to 0.85 | |
| 0 to 0.030 |
| Chromium (Cr), % | 3.8 to 5.0 | |
| 17 to 19 |
| Cobalt (Co), % | 7.0 to 9.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 60.6 to 68.3 | |
| 63.9 to 72 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.5 to 1.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 8.0 to 10 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 17.5 to 19 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.4 | |
| 0 |