SAE-AISI T5 Steel vs. R60802 Alloy
SAE-AISI T5 steel belongs to the iron alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI T5 steel and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 98 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 80 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 860 to 2140 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 270 |
| Thermal Conductivity, W/m-K | 21 | |
| 22 |
| Thermal Expansion, µm/m-K | 11 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.4 | |
| 6.5 |
| Embodied Water, L/kg | 140 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 25 to 63 | |
| 18 |
| Strength to Weight: Bending, points | 21 to 39 | |
| 19 |
| Thermal Diffusivity, mm2/s | 5.5 | |
| 12 |
| Thermal Shock Resistance, points | 26 to 66 | |
| 53 |
Alloy Composition
| Carbon (C), % | 0.75 to 0.85 | |
| 0 |
| Chromium (Cr), % | 3.8 to 5.0 | |
| 0.050 to 0.15 |
| Cobalt (Co), % | 7.0 to 9.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 60.6 to 68.3 | |
| 0.070 to 0.2 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 1.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0.030 to 0.080 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.2 to 1.7 |
| Tungsten (W), % | 17.5 to 19 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.4 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 97.8 to 98.7 |
| Residuals, % | 0 | |
| 0 to 0.11 |