SAE-AISI T6 Steel vs. C15500 Copper

SAE-AISI T6 steel belongs to the iron alloys classification, while C15500 copper belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI T6 steel and the bottom bar is C15500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
120
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 81
43
Tensile Strength: Ultimate (UTS), MPa 880 to 2150
280 to 550

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Melting Completion (Liquidus), °C 1830
1080
Melting Onset (Solidus), °C 1770
1080
Specific Heat Capacity, J/kg-K 400
390
Thermal Conductivity, W/m-K 18
350
Thermal Expansion, µm/m-K 12
17

Otherwise Unclassified Properties

Base Metal Price, % relative 70
33
Density, g/cm3 9.5
8.9
Embodied Carbon, kg CO2/kg material 11
2.7
Embodied Energy, MJ/kg 170
42
Embodied Water, L/kg 160
360

Common Calculations

Stiffness to Weight: Axial, points 12
7.2
Stiffness to Weight: Bending, points 21
18
Strength to Weight: Axial, points 26 to 63
8.6 to 17
Strength to Weight: Bending, points 21 to 39
11 to 17
Thermal Diffusivity, mm2/s 4.7
100
Thermal Shock Resistance, points 26 to 64
9.8 to 20

Alloy Composition

Carbon (C), % 0.75 to 0.85
0
Chromium (Cr), % 4.0 to 4.8
0
Cobalt (Co), % 11 to 13
0
Copper (Cu), % 0 to 0.25
99.75 to 99.853
Iron (Fe), % 55.9 to 63.5
0
Magnesium (Mg), % 0
0.080 to 0.13
Manganese (Mn), % 0.2 to 0.4
0
Molybdenum (Mo), % 0.4 to 1.0
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0.040 to 0.080
Silicon (Si), % 0.2 to 0.4
0
Silver (Ag), % 0
0.027 to 0.1
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 18.5 to 21
0
Vanadium (V), % 1.5 to 2.1
0
Residuals, % 0
0 to 0.2