SAE-AISI T8 Steel vs. EN 1.5507 Steel

Both SAE-AISI T8 steel and EN 1.5507 steel are iron alloys. They have 73% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI T8 steel and the bottom bar is EN 1.5507 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 780 to 2140
450 to 880

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1730
1460
Melting Onset (Solidus), °C 1670
1420
Specific Heat Capacity, J/kg-K 420
470
Thermal Conductivity, W/m-K 18
49
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 45
2.0
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 10
1.4
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 120
49

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 24 to 66
16 to 31
Strength to Weight: Bending, points 21 to 41
17 to 26
Thermal Diffusivity, mm2/s 4.8
13
Thermal Shock Resistance, points 24 to 66
13 to 26

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.080
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.75 to 0.85
0.21 to 0.25
Chromium (Cr), % 3.8 to 4.5
0.25 to 0.35
Cobalt (Co), % 4.3 to 5.8
0
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 69.3 to 75.4
97.8 to 98.7
Manganese (Mn), % 0.2 to 0.4
0.8 to 1.0
Molybdenum (Mo), % 0.4 to 1.0
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0.2 to 0.4
0 to 0.15
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.060
Tungsten (W), % 13.3 to 14.8
0
Vanadium (V), % 1.8 to 2.4
0