Sandstone vs. Borosilicate Glass
Sandstone belongs to the natural stone classification, while borosilicate glass belongs to the glass and glass-ceramics. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is sandstone and the bottom bar is borosilicate glass.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 120 | |
| 2000 |
| Elastic (Young's, Tensile) Modulus, GPa | 38 | |
| 67 to 80 |
| Poisson's Ratio | 0.25 | |
| 0.21 |
| Tensile Strength: Ultimate (UTS), MPa | 4.0 | |
| 280 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 400 | |
| 360 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 830 |
| Thermal Conductivity, W/m-K | 5.6 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 10 | |
| 3.3 to 5.1 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 8.5 | |
| 5.0 to 34 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.6 | |
| 2.2 to 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 15 to 17 |
| Stiffness to Weight: Bending, points | 43 | |
| 55 to 61 |
| Strength to Weight: Axial, points | 0.43 | |
| 30 to 35 |
| Strength to Weight: Bending, points | 2.1 | |
| 36 to 43 |
| Thermal Diffusivity, mm2/s | 2.4 | |
| 0.54 to 0.63 |
| Thermal Shock Resistance, points | 0.75 | |
| 50 to 91 |