SiAlON vs. Sandstone
SiAlON belongs to the non-oxide engineering ceramics classification, while sandstone belongs to the natural stone. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SiAlON and the bottom bar is sandstone.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 2620 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 290 | |
| 38 |
| Poisson's Ratio | 0.23 | |
| 0.25 |
| Shear Modulus, GPa | 120 | |
| 15 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 4.0 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1200 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 880 |
| Thermal Conductivity, W/m-K | 19 | |
| 5.6 |
| Thermal Expansion, µm/m-K | 3.6 | |
| 10 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 8.3 | |
| 8.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.3 | |
| 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 50 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 67 | |
| 43 |
| Strength to Weight: Axial, points | 16 | |
| 0.43 |
| Strength to Weight: Bending, points | 22 | |
| 2.1 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 2.4 |
| Thermal Shock Resistance, points | 13 | |
| 0.75 |