SAN vs. PP Homopolymer
Both SAN and PP homopolymer are thermoplastics. There are 8 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAN and the bottom bar is PP homopolymer.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 to 1.4 | |
| 0.91 to 1.2 |
| Elongation at Break, % | 2.5 | |
| 3.0 to 80 |
| Flexural Modulus, GPa | 3.8 to 13 | |
| 1.5 to 7.0 |
| Impact Strength: Notched Izod, J/m | 23 to 60 | |
| 42 to 95 |
| Specific Heat Capacity, J/kg-K | 1070 to 1380 | |
| 1230 to 1900 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 36 to 40 | |
| 27 to 37 |
| Tensile Strength: Ultimate (UTS), MPa | 74 to 130 | |
| 36 to 93 |