Thallium Bromoiodide vs. Zirconia
Thallium bromoiodide belongs to the non-glass optical ceramics classification, while zirconia belongs to the oxide-based engineering ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is thallium bromoiodide and the bottom bar is zirconia.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.4 | |
| 5.7 to 6.0 |
| Elastic (Young's, Tensile) Modulus, GPa | 31 | |
| 190 to 200 |
| Poisson's Ratio | 0.37 | |
| 0.25 to 0.29 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 400 to 510 |
| Stiffness to Weight: Axial, points | 2.3 | |
| 19 |
| Stiffness to Weight: Bending, points | 14 | |
| 33 to 34 |
| Thermal Conductivity, W/m-K | 0.55 | |
| 2.2 to 4.3 |
| Thermal Diffusivity, mm2/s | 0.5 | |
| 0.73 to 1.8 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 8.8 to 9.5 |