Thermoplastic PI vs. PVF
Both thermoplastic PI and PVF are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is thermoplastic PI and the bottom bar is PVF.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.5 | |
| 1.4 |
| Flexural Strength, MPa | 170 to 330 | |
| 90 |
| Glass Transition Temperature, °C | 260 | |
| -20 |
| Limiting Oxygen Index (LOI), % | 35 | |
| 23 |
| Maximum Temperature: Autoignition, °C | 600 | |
| 480 |
| Maximum Temperature: Decomposition, °C | 530 | |
| 360 |
| Specific Heat Capacity, J/kg-K | 970 to 1100 | |
| 1300 |
| Strength to Weight: Axial, points | 22 to 42 | |
| 13 |
| Strength to Weight: Bending, points | 36 to 57 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 110 to 220 | |
| 65 |