Thermoset PI vs. PAI
Thermoset PI belongs to the thermoset plastics classification, while PAI belongs to the thermoplastics. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is thermoset PI and the bottom bar is PAI.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 120 to 210 | |
| 260 to 300 |
| Elongation at Break, % | 2.0 to 5.9 | |
| 3.0 to 12 |
| Flexural Modulus, GPa | 3.1 to 4.8 | |
| 4.0 to 6.8 |
| Flexural Strength, MPa | 60 to 100 | |
| 160 to 320 |
| Impact Strength: Notched Izod, J/m | 21 to 43 | |
| 45 to 140 |
| Tensile Strength: Ultimate (UTS), MPa | 37 to 81 | |
| 100 to 180 |
Thermal Properties
| Glass Transition Temperature, °C | 360 | |
| 280 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 370 | |
| 280 |
| Maximum Temperature: Autoignition, °C | 380 | |
| 530 |
| Maximum Temperature: Decomposition, °C | 330 | |
| 490 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 260 |
| Specific Heat Capacity, J/kg-K | 1130 | |
| 910 to 1000 |
| Thermal Conductivity, W/m-K | 0.29 to 1.7 | |
| 0.26 to 0.53 |
| Thermal Expansion, µm/m-K | 38 to 54 | |
| 15 to 34 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.4 to 1.6 |
| Limiting Oxygen Index (LOI), % | 40 | |
| 45 |
| Water Absorption After 24 Hours, % | 0.14 to 0.24 | |
| 0.3 to 0.4 |
| Water Absorption At Saturation, % | 3.6 | |
| 1.5 to 1.7 |
Common Calculations
| Strength to Weight: Axial, points | 6.5 to 16 | |
| 19 to 34 |
| Strength to Weight: Bending, points | 16 to 30 | |
| 33 to 49 |
| Thermal Diffusivity, mm2/s | 0.18 to 0.95 | |
| 0.16 to 0.41 |