C-310 Titania-based Ceramic vs. Alumina-lime-silica Glass
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while alumina-lime-silica glass belongs to the glass and glass-ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is alumina-lime-silica glass.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 2.8 |
| Dielectric Constant (Relative Permittivity) At 1 Hz | 70 | |
| 6.5 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 34 |
| Electrical Dissipation At 1 Hz | 0.0056 | |
| 0.0022 |
| Electrical Dissipation At 1 MHz | 0.0018 | |
| 0.0026 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 12 |
| Flexural Strength, MPa | 75 | |
| 46 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 4.3 |