C-310 Titania-based Ceramic vs. Zirconia
Both C-310 titania-based ceramic and zirconia are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is zirconia.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 5.7 to 6.0 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 7.7 to 9.0 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 4.5 to 11 |
| Flexural Strength, MPa | 75 | |
| 630 to 970 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 400 to 510 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 2.2 to 4.3 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 0.73 to 1.8 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 8.8 to 9.5 |