Titanium 15-3-3-3 vs. Grade 29 Titanium
Both titanium 15-3-3-3 and grade 29 titanium are titanium alloys. They have 83% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is titanium 15-3-3-3 and the bottom bar is grade 29 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 5.7 to 8.0 | |
| 6.8 to 11 |
| Fatigue Strength, MPa | 610 to 710 | |
| 460 to 510 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Shear Strength, MPa | 660 to 810 | |
| 550 to 560 |
| Tensile Strength: Ultimate (UTS), MPa | 1120 to 1390 | |
| 930 to 940 |
| Tensile Strength: Yield (Proof), MPa | 1100 to 1340 | |
| 850 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 340 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1610 |
| Melting Onset (Solidus), °C | 1560 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 560 |
| Thermal Conductivity, W/m-K | 8.1 | |
| 7.3 |
| Thermal Expansion, µm/m-K | 9.8 | |
| 9.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.2 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.3 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 36 |
| Density, g/cm3 | 4.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 59 | |
| 39 |
| Embodied Energy, MJ/kg | 950 | |
| 640 |
| Embodied Water, L/kg | 260 | |
| 410 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 89 | |
| 62 to 100 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 35 |
| Strength to Weight: Axial, points | 64 to 80 | |
| 58 to 59 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 47 to 48 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 2.9 |
| Thermal Shock Resistance, points | 79 to 98 | |
| 68 to 69 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 3.5 | |
| 5.5 to 6.5 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.080 |
| Chromium (Cr), % | 2.5 to 3.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.25 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 to 0.13 |
| Ruthenium (Ru), % | 0 | |
| 0.080 to 0.14 |
| Tin (Sn), % | 2.5 to 3.5 | |
| 0 |
| Titanium (Ti), % | 72.6 to 78.5 | |
| 88 to 90.9 |
| Vanadium (V), % | 14 to 16 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |