Titanium 15-3-3-3 vs. S17700 Stainless Steel
Titanium 15-3-3-3 belongs to the titanium alloys classification, while S17700 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is titanium 15-3-3-3 and the bottom bar is S17700 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 5.7 to 8.0 | |
| 1.0 to 23 |
| Fatigue Strength, MPa | 610 to 710 | |
| 290 to 560 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 39 | |
| 76 |
| Shear Strength, MPa | 660 to 810 | |
| 740 to 940 |
| Tensile Strength: Ultimate (UTS), MPa | 1120 to 1390 | |
| 1180 to 1650 |
| Tensile Strength: Yield (Proof), MPa | 1100 to 1340 | |
| 430 to 1210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 890 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1440 |
| Melting Onset (Solidus), °C | 1560 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 8.1 | |
| 15 |
| Thermal Expansion, µm/m-K | 9.8 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.2 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.3 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 13 |
| Density, g/cm3 | 4.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 59 | |
| 2.8 |
| Embodied Energy, MJ/kg | 950 | |
| 40 |
| Embodied Water, L/kg | 260 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 89 | |
| 15 to 210 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 32 | |
| 25 |
| Strength to Weight: Axial, points | 64 to 80 | |
| 42 to 59 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 32 to 40 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 4.1 |
| Thermal Shock Resistance, points | 79 to 98 | |
| 39 to 54 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0.75 to 1.5 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.090 |
| Chromium (Cr), % | 2.5 to 3.5 | |
| 16 to 18 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 70.5 to 76.8 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 6.5 to 7.8 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 2.5 to 3.5 | |
| 0 |
| Titanium (Ti), % | 72.6 to 78.5 | |
| 0 |
| Vanadium (V), % | 14 to 16 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |