Titanium 6-2-4-2 vs. C63020 Bronze
Titanium 6-2-4-2 belongs to the titanium alloys classification, while C63020 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is titanium 6-2-4-2 and the bottom bar is C63020 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 8.6 | |
| 6.8 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 44 |
| Shear Strength, MPa | 560 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 950 | |
| 1020 |
| Tensile Strength: Yield (Proof), MPa | 880 | |
| 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 300 | |
| 230 |
| Melting Completion (Liquidus), °C | 1590 | |
| 1070 |
| Melting Onset (Solidus), °C | 1540 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 450 |
| Thermal Conductivity, W/m-K | 6.9 | |
| 40 |
| Thermal Expansion, µm/m-K | 9.5 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 42 | |
| 29 |
| Density, g/cm3 | 4.6 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 32 | |
| 3.6 |
| Embodied Energy, MJ/kg | 520 | |
| 58 |
| Embodied Water, L/kg | 210 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 | |
| 63 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3640 | |
| 2320 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.0 |
| Stiffness to Weight: Bending, points | 34 | |
| 20 |
| Strength to Weight: Axial, points | 57 | |
| 34 |
| Strength to Weight: Bending, points | 46 | |
| 27 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 11 |
| Thermal Shock Resistance, points | 67 | |
| 35 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 6.5 | |
| 10 to 11 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.050 |
| Cobalt (Co), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 | |
| 74.7 to 81.8 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 4.0 to 5.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 1.8 to 2.2 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 4.2 to 6.0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.15 | |
| 0 |
| Silicon (Si), % | 0.060 to 0.12 | |
| 0 |
| Tin (Sn), % | 1.8 to 2.2 | |
| 0 to 0.25 |
| Titanium (Ti), % | 83.7 to 87.2 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.3 |
| Zirconium (Zr), % | 3.6 to 4.4 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |