Titanium 6-6-2 vs. Z13004 Zinc
Titanium 6-6-2 belongs to the titanium alloys classification, while Z13004 zinc belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is titanium 6-6-2 and the bottom bar is Z13004 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 87 |
| Elongation at Break, % | 6.7 to 9.0 | |
| 30 |
| Poisson's Ratio | 0.32 | |
| 0.25 |
| Shear Modulus, GPa | 44 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 to 1370 | |
| 93 |
| Tensile Strength: Yield (Proof), MPa | 1040 to 1230 | |
| 76 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 90 |
| Melting Completion (Liquidus), °C | 1610 | |
| 410 |
| Melting Onset (Solidus), °C | 1560 | |
| 390 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 390 |
| Thermal Conductivity, W/m-K | 5.5 | |
| 110 |
| Thermal Expansion, µm/m-K | 9.4 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.1 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 11 |
| Density, g/cm3 | 4.8 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 29 | |
| 2.8 |
| Embodied Energy, MJ/kg | 470 | |
| 53 |
| Embodied Water, L/kg | 200 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 89 to 99 | |
| 26 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 34 | |
| 23 |
| Strength to Weight: Axial, points | 66 to 79 | |
| 3.9 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 7.0 |
| Thermal Diffusivity, mm2/s | 2.1 | |
| 44 |
| Thermal Shock Resistance, points | 75 to 90 | |
| 2.9 |
Alloy Composition
| Aluminum (Al), % | 5.0 to 6.0 | |
| 0 to 0.0020 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0030 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 0 to 0.0030 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 0 to 0.0030 |
| Lead (Pb), % | 0 | |
| 0 to 0.0030 |
| Molybdenum (Mo), % | 5.0 to 6.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 to 0.0010 |
| Titanium (Ti), % | 82.8 to 87.8 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 99.985 to 100 |
| Residuals, % | 0 to 0.4 | |
| 0 |