Titanium 6-6-2 vs. C67600 Bronze
Titanium 6-6-2 belongs to the titanium alloys classification, while C67600 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is titanium 6-6-2 and the bottom bar is C67600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 6.7 to 9.0 | |
| 13 to 33 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Shear Strength, MPa | 670 to 800 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 to 1370 | |
| 430 to 570 |
| Tensile Strength: Yield (Proof), MPa | 1040 to 1230 | |
| 170 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 120 |
| Melting Completion (Liquidus), °C | 1610 | |
| 890 |
| Melting Onset (Solidus), °C | 1560 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 380 |
| Thermal Conductivity, W/m-K | 5.5 | |
| 110 |
| Thermal Expansion, µm/m-K | 9.4 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.1 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 23 |
| Density, g/cm3 | 4.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 29 | |
| 2.8 |
| Embodied Energy, MJ/kg | 470 | |
| 47 |
| Embodied Water, L/kg | 200 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 89 to 99 | |
| 63 to 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 34 | |
| 20 |
| Strength to Weight: Axial, points | 66 to 79 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 2.1 | |
| 35 |
| Thermal Shock Resistance, points | 75 to 90 | |
| 14 to 19 |
Alloy Composition
| Aluminum (Al), % | 5.0 to 6.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 57 to 60 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 0.4 to 1.3 |
| Lead (Pb), % | 0 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Molybdenum (Mo), % | 5.0 to 6.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0.5 to 1.5 |
| Titanium (Ti), % | 82.8 to 87.8 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 35.2 to 41.6 |
| Residuals, % | 0 | |
| 0 to 0.5 |