Titanium 6-7 vs. EN 1.7117 Steel
Titanium 6-7 belongs to the titanium alloys classification, while EN 1.7117 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is titanium 6-7 and the bottom bar is EN 1.7117 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 45 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 660 to 1930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 300 | |
| 420 |
| Melting Completion (Liquidus), °C | 1700 | |
| 1440 |
| Melting Onset (Solidus), °C | 1650 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 2.6 |
| Density, g/cm3 | 5.1 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 34 | |
| 1.5 |
| Embodied Energy, MJ/kg | 540 | |
| 21 |
| Embodied Water, L/kg | 190 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 25 |
| Strength to Weight: Axial, points | 56 | |
| 24 to 69 |
| Strength to Weight: Bending, points | 44 | |
| 22 to 44 |
| Thermal Shock Resistance, points | 66 | |
| 20 to 58 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 6.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0.49 to 0.56 |
| Chromium (Cr), % | 0 | |
| 0.7 to 1.0 |
| Hydrogen (H), % | 0 to 0.0090 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 95.2 to 96.4 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 6.5 to 7.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.5 to 0.7 |
| Niobium (Nb), % | 6.5 to 7.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 1.2 to 1.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tantalum (Ta), % | 0 to 0.5 | |
| 0 |
| Titanium (Ti), % | 84.9 to 88 | |
| 0 |