Titanium Diboride vs. Machinable Glass-ceramic
Titanium diboride belongs to the non-oxide engineering ceramics classification, while machinable glass-ceramic belongs to the glass and glass-ceramics. There are 19 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is titanium diboride and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 3540 | |
| 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 290 | |
| 67 |
| Flexural Strength, MPa | 380 | |
| 96 |
| Fracture Toughness, MPa-m1/2 | 6.5 | |
| 2.5 |
| Knoop Hardness | 2800 | |
| 250 |
| Poisson's Ratio | 0.11 | |
| 0.29 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 84 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1270 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 790 |
| Thermal Conductivity, W/m-K | 58 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 8.0 | |
| 21 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | -6.5 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 35 | |
| 14 |
| Stiffness to Weight: Bending, points | 49 | |
| 51 |
| Strength to Weight: Axial, points | 17 | |
| 8.8 |
| Strength to Weight: Bending, points | 21 | |
| 16 |
| Thermal Diffusivity, mm2/s | 15 | |
| 0.56 |
| Thermal Shock Resistance, points | 8.7 | |
| 4.3 |