Tungsten Carbide vs. Hafnia
Tungsten carbide belongs to the non-oxide engineering ceramics classification, while hafnia belongs to the oxide-based engineering ceramics. There are 10 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is tungsten carbide and the bottom bar is hafnia.
Metric UnitsUS Customary Units
Material Properties
Density, g/cm3 | 15 | |
9.7 |
Elastic (Young's, Tensile) Modulus, GPa | 630 | |
57 |
Electrical Resistivity Order of Magnitude, 10x Ω-m | 0.75 | |
9.0 |
Maximum Temperature: Mechanical, °C | 1000 | |
2800 |
Specific Heat Capacity, J/kg-K | 280 | |
120 |
Stiffness to Weight: Axial, points | 24 | |
3.3 |
Stiffness to Weight: Bending, points | 20 | |
13 |
Thermal Conductivity, W/m-K | 85 | |
1.1 |
Thermal Diffusivity, mm2/s | 21 | |
0.95 |
Thermal Expansion, µm/m-K | 5.4 | |
6.0 |