Type 1 Magnetic Alloy vs. SAE-AISI 4130 Steel
Both Type 1 magnetic alloy and SAE-AISI 4130 steel are iron alloys. They have 55% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Type 1 magnetic alloy and the bottom bar is SAE-AISI 4130 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 4.0 to 38 | |
| 13 to 26 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 830 | |
| 530 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 220 to 790 | |
| 440 to 980 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.1 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 2.4 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 1.5 |
| Embodied Energy, MJ/kg | 77 | |
| 20 |
| Embodied Water, L/kg | 130 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 to 150 | |
| 83 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1690 | |
| 500 to 2550 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 28 | |
| 19 to 37 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 19 to 29 |
| Thermal Shock Resistance, points | 16 to 26 | |
| 16 to 31 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.28 to 0.33 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0.8 to 1.1 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 50.7 to 56.5 | |
| 97.3 to 98.2 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0.4 to 0.6 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 43.5 to 46.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.040 |