Type 1 Magnetic Alloy vs. K93600 Alloy
Both Type 1 magnetic alloy and K93600 alloy are iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is Type 1 magnetic alloy and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 4.0 to 38 | |
| 5.0 to 35 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 830 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 220 to 790 | |
| 280 to 750 |
Thermal Properties
| Curie Temperature, °C | 440 | |
| 250 |
| Melting Onset (Solidus), °C | 1370 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 520 |
| Thermal Expansion, µm/m-K | 12 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.1 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 to 150 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1690 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 12 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 28 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 16 to 26 | |
| 34 to 57 |