Type 1 Magnetic Alloy vs. S35000 Stainless Steel
Both Type 1 magnetic alloy and S35000 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is Type 1 magnetic alloy and the bottom bar is S35000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 4.0 to 38 | |
| 2.3 to 14 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 830 | |
| 1300 to 1570 |
| Tensile Strength: Yield (Proof), MPa | 220 to 790 | |
| 660 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.1 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 14 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 3.2 |
| Embodied Energy, MJ/kg | 77 | |
| 44 |
| Embodied Water, L/kg | 130 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 to 150 | |
| 28 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1690 | |
| 1070 to 3360 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 28 | |
| 46 to 56 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 34 to 38 |
| Thermal Shock Resistance, points | 16 to 26 | |
| 42 to 51 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 0 to 0.3 | |
| 16 to 17 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 50.7 to 56.5 | |
| 72.7 to 76.9 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 43.5 to 46.5 | |
| 4.0 to 5.0 |
| Nitrogen (N), % | 0 | |
| 0.070 to 0.13 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |