Type 1 Niobium vs. 772.0 Aluminum
Type 1 niobium belongs to the otherwise unclassified metals classification, while 772.0 aluminum belongs to the aluminum alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is Type 1 niobium and the bottom bar is 772.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 69 |
| Elongation at Break, % | 29 | |
| 6.3 to 8.4 |
| Poisson's Ratio | 0.4 | |
| 0.32 |
| Shear Modulus, GPa | 38 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 260 to 320 |
| Tensile Strength: Yield (Proof), MPa | 82 | |
| 220 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 870 |
| Thermal Conductivity, W/m-K | 52 | |
| 150 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 24 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 3.0 |
| Embodied Water, L/kg | 160 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 | |
| 16 to 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 32 | |
| 350 to 430 |
| Stiffness to Weight: Axial, points | 6.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 46 |
| Strength to Weight: Axial, points | 4.6 | |
| 25 to 31 |
| Strength to Weight: Bending, points | 7.1 | |
| 31 to 36 |
| Thermal Diffusivity, mm2/s | 23 | |
| 58 |
| Thermal Shock Resistance, points | 13 | |
| 11 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 91.2 to 93.2 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.060 to 0.2 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Hafnium (Hf), % | 0 to 0.020 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0 | |
| 0.6 to 0.8 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 to 0.010 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Niobium (Nb), % | 99.7 to 100 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.15 |
| Tantalum (Ta), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0.1 to 0.2 |
| Tungsten (W), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 6.0 to 7.0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |