Type 1 Niobium vs. 851.0 Aluminum
Type 1 niobium belongs to the otherwise unclassified metals classification, while 851.0 aluminum belongs to the aluminum alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is Type 1 niobium and the bottom bar is 851.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 69 |
| Elongation at Break, % | 29 | |
| 3.9 to 9.1 |
| Poisson's Ratio | 0.4 | |
| 0.33 |
| Shear Modulus, GPa | 38 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 130 to 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 410 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 850 |
| Thermal Conductivity, W/m-K | 52 | |
| 180 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 3.1 |
| Embodied Water, L/kg | 160 | |
| 1140 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 45 |
| Strength to Weight: Axial, points | 4.6 | |
| 12 to 13 |
| Strength to Weight: Bending, points | 7.1 | |
| 19 to 20 |
| Thermal Diffusivity, mm2/s | 23 | |
| 69 |
| Thermal Shock Resistance, points | 13 | |
| 6.1 to 6.3 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 86.6 to 91.5 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.7 to 1.3 |
| Hafnium (Hf), % | 0 to 0.020 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 to 0.010 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0.3 to 0.7 |
| Niobium (Nb), % | 99.7 to 100 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 2.0 to 3.0 |
| Tantalum (Ta), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 0 | |
| 5.5 to 7.0 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 to 0.2 |
| Tungsten (W), % | 0 to 0.030 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |