Type 2 Magnetic Alloy vs. Grade CX2M Nickel
Type 2 magnetic alloy belongs to the iron alloys classification, while grade CX2M nickel belongs to the nickel alloys. They have 50% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is grade CX2M nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 2.0 to 38 | |
| 45 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
| 550 |
| Tensile Strength: Yield (Proof), MPa | 260 to 870 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1500 |
| Melting Onset (Solidus), °C | 1370 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 430 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 65 |
| Density, g/cm3 | 8.4 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 12 |
| Embodied Energy, MJ/kg | 81 | |
| 160 |
| Embodied Water, L/kg | 140 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 160 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 2010 | |
| 220 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 17 to 30 | |
| 18 |
| Strength to Weight: Bending, points | 17 to 25 | |
| 17 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 to 0.3 | |
| 22 to 24 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 48.2 to 53 | |
| 0 to 1.5 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 15 to 16.5 |
| Nickel (Ni), % | 47 to 49 | |
| 56.4 to 63 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |