Type 2 Magnetic Alloy vs. Monel K-500
Type 2 magnetic alloy belongs to the iron alloys classification, while Monel K-500 belongs to the nickel alloys. They have 50% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is Monel K-500.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 160 |
| Elongation at Break, % | 2.0 to 38 | |
| 25 to 36 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 72 | |
| 61 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
| 640 to 1100 |
| Tensile Strength: Yield (Proof), MPa | 260 to 870 | |
| 310 to 880 |
Thermal Properties
| Curie Temperature, °C | 480 | |
| -67 |
| Latent Heat of Fusion, J/g | 270 | |
| 270 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1350 |
| Melting Onset (Solidus), °C | 1370 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 440 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.9 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.2 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 50 |
| Density, g/cm3 | 8.4 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 8.1 |
| Embodied Energy, MJ/kg | 81 | |
| 120 |
| Embodied Water, L/kg | 140 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 160 | |
| 180 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 2010 | |
| 300 to 2420 |
| Stiffness to Weight: Axial, points | 12 | |
| 10 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 30 | |
| 21 to 35 |
| Strength to Weight: Bending, points | 17 to 25 | |
| 19 to 27 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 21 to 36 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.3 to 3.2 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.18 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 27 to 33 |
| Iron (Fe), % | 48.2 to 53 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 47 to 49 | |
| 63 to 70.4 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.35 to 0.85 |