Type 2 Magnetic Alloy vs. SAE-AISI P6 Steel
Both Type 2 magnetic alloy and SAE-AISI P6 steel are iron alloys. They have 55% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is SAE-AISI P6 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
| 630 to 1930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.9 | |
| 7.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.2 | |
| 9.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 4.6 |
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 1.8 |
| Embodied Energy, MJ/kg | 81 | |
| 24 |
| Embodied Water, L/kg | 140 | |
| 59 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 30 | |
| 22 to 68 |
| Strength to Weight: Bending, points | 17 to 25 | |
| 21 to 44 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 21 to 63 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 to 0.3 | |
| 1.3 to 1.8 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 48.2 to 53 | |
| 92.9 to 95 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0.35 to 0.7 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 47 to 49 | |
| 3.3 to 3.8 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |