Type 2 Magnetic Alloy vs. Type 2 Pewter
Type 2 magnetic alloy belongs to the iron alloys classification, while Type 2 pewter belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is Type 2 pewter.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 52 |
| Poisson's Ratio | 0.3 | |
| 0.35 |
| Shear Modulus, GPa | 72 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
| 52 to 68 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 69 |
| Melting Completion (Liquidus), °C | 1420 | |
| 300 |
| Melting Onset (Solidus), °C | 1370 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 220 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 75 |
| Density, g/cm3 | 8.4 | |
| 7.3 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 12 |
| Embodied Energy, MJ/kg | 81 | |
| 210 |
| Embodied Water, L/kg | 140 | |
| 1220 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 3.9 |
| Stiffness to Weight: Bending, points | 23 | |
| 17 |
| Strength to Weight: Axial, points | 17 to 30 | |
| 2.0 to 2.6 |
| Strength to Weight: Bending, points | 17 to 25 | |
| 4.3 to 5.1 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 3.4 to 4.4 |
Alloy Composition
| Antimony (Sb), % | 0 | |
| 5.0 to 7.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 48.2 to 53 | |
| 0 to 0.015 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 47 to 49 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 90 to 93 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |