Type 2 Magnetic Alloy vs. C26000 Brass
Type 2 magnetic alloy belongs to the iron alloys classification, while C26000 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is C26000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
110 |
Elongation at Break, % | 2.0 to 38 | |
2.5 to 66 |
Poisson's Ratio | 0.3 | |
0.31 |
Shear Modulus, GPa | 72 | |
41 |
Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
320 to 680 |
Tensile Strength: Yield (Proof), MPa | 260 to 870 | |
110 to 570 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
180 |
Melting Completion (Liquidus), °C | 1420 | |
950 |
Melting Onset (Solidus), °C | 1370 | |
920 |
Specific Heat Capacity, J/kg-K | 460 | |
390 |
Thermal Expansion, µm/m-K | 12 | |
20 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 3.9 | |
28 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 4.2 | |
31 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 33 | |
25 |
Density, g/cm3 | 8.4 | |
8.2 |
Embodied Carbon, kg CO2/kg material | 5.9 | |
2.7 |
Embodied Energy, MJ/kg | 81 | |
45 |
Embodied Water, L/kg | 140 | |
320 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 160 | |
6.1 to 420 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 2010 | |
51 to 1490 |
Stiffness to Weight: Axial, points | 12 | |
7.2 |
Stiffness to Weight: Bending, points | 23 | |
19 |
Strength to Weight: Axial, points | 17 to 30 | |
11 to 23 |
Strength to Weight: Bending, points | 17 to 25 | |
13 to 21 |
Thermal Shock Resistance, points | 16 to 29 | |
11 to 23 |
Alloy Composition
Bismuth (Bi), % | 0 | |
0 to 0.0059 |
Carbon (C), % | 0 to 0.050 | |
0 |
Chromium (Cr), % | 0 to 0.3 | |
0 |
Cobalt (Co), % | 0 to 0.5 | |
0 |
Copper (Cu), % | 0 to 0.3 | |
68.5 to 71.5 |
Iron (Fe), % | 48.2 to 53 | |
0 to 0.050 |
Lead (Pb), % | 0 | |
0 to 0.070 |
Manganese (Mn), % | 0 to 0.8 | |
0 |
Molybdenum (Mo), % | 0 to 0.3 | |
0 |
Nickel (Ni), % | 47 to 49 | |
0 |
Phosphorus (P), % | 0 to 0.010 | |
0 |
Silicon (Si), % | 0 to 0.5 | |
0 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Zinc (Zn), % | 0 | |
28.1 to 31.5 |
Residuals, % | 0 | |
0 to 0.3 |