Type 2 Magnetic Alloy vs. N08221 Nickel
Type 2 magnetic alloy belongs to the iron alloys classification, while N08221 nickel belongs to the nickel alloys. They have 71% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is N08221 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 2.0 to 38 | |
| 34 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 910 | |
| 610 |
| Tensile Strength: Yield (Proof), MPa | 260 to 870 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 310 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1440 |
| Melting Onset (Solidus), °C | 1370 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 44 |
| Density, g/cm3 | 8.4 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 5.9 | |
| 7.9 |
| Embodied Energy, MJ/kg | 81 | |
| 110 |
| Embodied Water, L/kg | 140 | |
| 240 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 160 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 2010 | |
| 170 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 30 | |
| 21 |
| Strength to Weight: Bending, points | 17 to 25 | |
| 19 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.025 |
| Chromium (Cr), % | 0 to 0.3 | |
| 20 to 22 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 48.2 to 53 | |
| 22 to 33.9 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 5.0 to 6.5 |
| Nickel (Ni), % | 47 to 49 | |
| 39 to 46 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.6 to 1.0 |