Type 2 Magnetic Alloy vs. R05240 Alloy

Type 2 magnetic alloy belongs to the iron alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is Type 2 magnetic alloy and the bottom bar is R05240 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
150
Elongation at Break, % 2.0 to 38
25
Poisson's Ratio 0.3
0.36
Shear Modulus, GPa 72
57
Tensile Strength: Ultimate (UTS), MPa 510 to 910
270
Tensile Strength: Yield (Proof), MPa 260 to 870
170

Thermal Properties

Latent Heat of Fusion, J/g 270
210
Specific Heat Capacity, J/kg-K 460
190
Thermal Expansion, µm/m-K 12
6.8

Otherwise Unclassified Properties

Density, g/cm3 8.4
14
Embodied Water, L/kg 140
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 18 to 160
59
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 2010
90
Stiffness to Weight: Axial, points 12
6.3
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 17 to 30
5.4
Strength to Weight: Bending, points 17 to 25
6.8
Thermal Shock Resistance, points 16 to 29
18

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.010
Chromium (Cr), % 0 to 0.3
0
Cobalt (Co), % 0 to 0.5
0
Copper (Cu), % 0 to 0.3
0
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 48.2 to 53
0 to 0.010
Manganese (Mn), % 0 to 0.8
0
Molybdenum (Mo), % 0 to 0.3
0 to 0.020
Nickel (Ni), % 47 to 49
0 to 0.010
Niobium (Nb), % 0
35 to 42
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0 to 0.5
0 to 0.0050
Sulfur (S), % 0 to 0.030
0
Tantalum (Ta), % 0
57.9 to 65
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0 to 0.050