Type 2 Pewter vs. ACI-ASTM CB7Cu-2 Steel
Type 2 pewter belongs to the otherwise unclassified metals classification, while ACI-ASTM CB7Cu-2 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is Type 2 pewter and the bottom bar is ACI-ASTM CB7Cu-2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 13 to 23 | |
300 to 420 |
Elastic (Young's, Tensile) Modulus, GPa | 52 | |
190 |
Poisson's Ratio | 0.35 | |
0.28 |
Shear Modulus, GPa | 19 | |
75 |
Tensile Strength: Ultimate (UTS), MPa | 52 to 68 | |
960 to 1350 |
Thermal Properties
Latent Heat of Fusion, J/g | 69 | |
280 |
Melting Completion (Liquidus), °C | 300 | |
1430 |
Melting Onset (Solidus), °C | 240 | |
1380 |
Specific Heat Capacity, J/kg-K | 220 | |
480 |
Thermal Expansion, µm/m-K | 21 | |
11 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 75 | |
13 |
Density, g/cm3 | 7.3 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 12 | |
2.6 |
Embodied Energy, MJ/kg | 210 | |
38 |
Embodied Water, L/kg | 1220 | |
130 |
Common Calculations
Stiffness to Weight: Axial, points | 3.9 | |
14 |
Stiffness to Weight: Bending, points | 17 | |
25 |
Strength to Weight: Axial, points | 2.0 to 2.6 | |
34 to 48 |
Strength to Weight: Bending, points | 4.3 to 5.1 | |
28 to 35 |
Thermal Shock Resistance, points | 3.4 to 4.4 | |
32 to 45 |
Alloy Composition
Antimony (Sb), % | 5.0 to 7.5 | |
0 |
Arsenic (As), % | 0 to 0.050 | |
0 |
Carbon (C), % | 0 | |
0 to 0.070 |
Chromium (Cr), % | 0 | |
14 to 15.5 |
Copper (Cu), % | 1.5 to 3.0 | |
2.5 to 3.2 |
Iron (Fe), % | 0 to 0.015 | |
73.6 to 79 |
Lead (Pb), % | 0 to 0.050 | |
0 |
Manganese (Mn), % | 0 | |
0 to 0.7 |
Nickel (Ni), % | 0 | |
4.5 to 5.5 |
Niobium (Nb), % | 0 | |
0 to 0.35 |
Nitrogen (N), % | 0 | |
0 to 0.050 |
Phosphorus (P), % | 0 | |
0 to 0.035 |
Silicon (Si), % | 0 | |
0 to 1.0 |
Sulfur (S), % | 0 | |
0 to 0.030 |
Tin (Sn), % | 90 to 93 | |
0 |
Zinc (Zn), % | 0 to 0.0050 | |
0 |