Type 2 Pewter vs. C95410 Bronze
Type 2 pewter belongs to the otherwise unclassified metals classification, while C95410 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is Type 2 pewter and the bottom bar is C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 13 to 23 | |
| 160 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 52 | |
| 120 |
| Poisson's Ratio | 0.35 | |
| 0.34 |
| Shear Modulus, GPa | 19 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 52 to 68 | |
| 620 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 69 | |
| 230 |
| Melting Completion (Liquidus), °C | 300 | |
| 1040 |
| Melting Onset (Solidus), °C | 240 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 440 |
| Thermal Expansion, µm/m-K | 21 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 28 |
| Density, g/cm3 | 7.3 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 3.3 |
| Embodied Energy, MJ/kg | 210 | |
| 54 |
| Embodied Water, L/kg | 1220 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.9 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 17 | |
| 20 |
| Strength to Weight: Axial, points | 2.0 to 2.6 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 4.3 to 5.1 | |
| 20 to 22 |
| Thermal Shock Resistance, points | 3.4 to 4.4 | |
| 22 to 26 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10 to 11.5 |
| Antimony (Sb), % | 5.0 to 7.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 1.5 to 3.0 | |
| 83 to 85.5 |
| Iron (Fe), % | 0 to 0.015 | |
| 3.0 to 5.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 1.5 to 2.5 |
| Tin (Sn), % | 90 to 93 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |