Type 2 Pewter vs. Z21721 Zinc
Type 2 pewter belongs to the otherwise unclassified metals classification, while Z21721 zinc belongs to the zinc alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is Type 2 pewter and the bottom bar is Z21721 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 52 | |
| 87 |
| Poisson's Ratio | 0.35 | |
| 0.25 |
| Shear Modulus, GPa | 19 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 52 to 68 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 69 | |
| 110 |
| Melting Completion (Liquidus), °C | 300 | |
| 410 |
| Melting Onset (Solidus), °C | 240 | |
| 390 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 390 |
| Thermal Expansion, µm/m-K | 21 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 11 |
| Density, g/cm3 | 7.3 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 2.8 |
| Embodied Energy, MJ/kg | 210 | |
| 53 |
| Embodied Water, L/kg | 1220 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.9 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 17 | |
| 22 |
| Strength to Weight: Axial, points | 2.0 to 2.6 | |
| 6.4 |
| Strength to Weight: Bending, points | 4.3 to 5.1 | |
| 9.6 |
| Thermal Shock Resistance, points | 3.4 to 4.4 | |
| 4.8 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0020 |
| Antimony (Sb), % | 5.0 to 7.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.050 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.070 |
| Copper (Cu), % | 1.5 to 3.0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.015 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 1.0 |
| Tin (Sn), % | 90 to 93 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 98.9 to 100 |