Type 3 Niobium vs. ASTM A216 Cast Steel
Type 3 niobium belongs to the otherwise unclassified metals classification, while ASTM A216 cast steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is Type 3 niobium and the bottom bar is ASTM A216 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 23 | |
| 25 to 27 |
| Poisson's Ratio | 0.4 | |
| 0.29 |
| Shear Modulus, GPa | 38 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 220 | |
| 500 to 570 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Conductivity, W/m-K | 42 | |
| 49 to 52 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Water, L/kg | 160 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 93 | |
| 140 to 250 |
| Stiffness to Weight: Axial, points | 6.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 7.2 | |
| 18 to 20 |
| Strength to Weight: Bending, points | 9.5 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 18 | |
| 13 to 14 |
| Thermal Shock Resistance, points | 21 | |
| 16 to 18 |