Type 3 Magnetic Alloy vs. Solder Alloy 112

Type 3 magnetic alloy belongs to the nickel alloys classification, while solder alloy 112 belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is Type 3 magnetic alloy and the bottom bar is solder alloy 112.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
33
Elongation at Break, % 43
35
Poisson's Ratio 0.31
0.4
Shear Modulus, GPa 70
12
Tensile Strength: Ultimate (UTS), MPa 550
41

Thermal Properties

Latent Heat of Fusion, J/g 290
41
Melting Completion (Liquidus), °C 1370
220
Melting Onset (Solidus), °C 1320
180
Specific Heat Capacity, J/kg-K 450
180
Thermal Expansion, µm/m-K 12
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
11
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
10

Otherwise Unclassified Properties

Density, g/cm3 8.7
9.3
Embodied Carbon, kg CO2/kg material 8.7
9.4
Embodied Energy, MJ/kg 120
160
Embodied Water, L/kg 220
830

Common Calculations

Stiffness to Weight: Axial, points 12
2.0
Stiffness to Weight: Bending, points 22
11
Strength to Weight: Axial, points 18
1.2
Strength to Weight: Bending, points 17
2.8
Thermal Shock Resistance, points 18
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.050
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 2.0 to 3.0
0
Cobalt (Co), % 0 to 0.5
0
Copper (Cu), % 4.0 to 6.0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 9.9 to 19
0 to 0.020
Lead (Pb), % 0
49 to 50.5
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 75 to 78
0 to 0.010
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0
0 to 0.0010