Type 4 Magnetic Alloy vs. EN 1.0213 Steel

Type 4 magnetic alloy belongs to the nickel alloys classification, while EN 1.0213 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Type 4 magnetic alloy and the bottom bar is EN 1.0213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 2.0 to 40
12 to 25
Fatigue Strength, MPa 220 to 400
160 to 240
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 420 to 630
230 to 270
Tensile Strength: Ultimate (UTS), MPa 620 to 1100
320 to 430
Tensile Strength: Yield (Proof), MPa 270 to 1040
220 to 330

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 440
470
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 60
1.8
Density, g/cm3 8.8
7.9
Embodied Carbon, kg CO2/kg material 10
1.4
Embodied Energy, MJ/kg 140
18
Embodied Water, L/kg 210
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22 to 200
33 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 2840
120 to 300
Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 19 to 35
11 to 15
Strength to Weight: Bending, points 18 to 27
13 to 16
Thermal Shock Resistance, points 21 to 37
10 to 14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.050
0.060 to 0.1
Chromium (Cr), % 0 to 0.3
0
Cobalt (Co), % 0 to 0.5
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 9.5 to 17.5
99.245 to 99.67
Manganese (Mn), % 0 to 0.8
0.25 to 0.45
Molybdenum (Mo), % 3.5 to 6.0
0
Nickel (Ni), % 79 to 82
0
Phosphorus (P), % 0 to 0.010
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.020
0 to 0.025

Comparable Variants