Type 4 Magnetic Alloy vs. Z21210 Zinc
Type 4 magnetic alloy belongs to the nickel alloys classification, while Z21210 zinc belongs to the zinc alloys. There are 10 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is Type 4 magnetic alloy and the bottom bar is Z21210 zinc.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 8.8 | |
| 7.1 |
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 35 |
| Melting Completion (Liquidus), °C | 1420 | |
| 420 |
| Melting Onset (Solidus), °C | 1370 | |
| 420 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 400 |
| Strength to Weight: Axial, points | 19 to 35 | |
| 5.7 to 6.4 |
| Strength to Weight: Bending, points | 18 to 27 | |
| 8.6 to 9.4 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1100 | |
| 150 to 170 |
| Thermal Expansion, µm/m-K | 11 | |
| 32 |