C10500 Copper vs. SAE-AISI 1022 Steel
C10500 copper belongs to the copper alloys classification, while SAE-AISI 1022 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C10500 copper and the bottom bar is SAE-AISI 1022 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 2.8 to 51 | |
| 17 to 26 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 73 |
| Shear Strength, MPa | 150 to 210 | |
| 310 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 400 | |
| 480 to 550 |
| Tensile Strength: Yield (Proof), MPa | 75 to 400 | |
| 260 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1460 |
| Melting Onset (Solidus), °C | 1080 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 390 | |
| 52 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 1.8 |
| Density, g/cm3 | 9.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 42 | |
| 18 |
| Embodied Water, L/kg | 350 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 90 | |
| 88 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 680 | |
| 190 to 530 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 6.8 to 12 | |
| 17 to 19 |
| Strength to Weight: Bending, points | 9.1 to 14 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 110 | |
| 14 |
| Thermal Shock Resistance, points | 7.8 to 14 | |
| 15 to 17 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.18 to 0.23 |
| Copper (Cu), % | 99.89 to 99.966 | |
| 0 |
| Iron (Fe), % | 0 | |
| 98.7 to 99.12 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Oxygen (O), % | 0 to 0.0010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silver (Ag), % | 0.034 to 0.060 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.050 | |
| 0 |