C11100 Copper vs. C19100 Copper
Both C11100 copper and C19100 copper are copper alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C11100 copper and the bottom bar is C19100 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 1.5 | |
| 17 to 37 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Shear Strength, MPa | 230 | |
| 170 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 460 | |
| 250 to 630 |
| Tensile Strength: Yield (Proof), MPa | 420 | |
| 75 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1080 |
| Melting Onset (Solidus), °C | 1070 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 390 | |
| 250 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 55 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 56 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 33 |
| Density, g/cm3 | 9.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 41 | |
| 43 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.6 | |
| 60 to 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 750 | |
| 24 to 1310 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 14 | |
| 7.7 to 20 |
| Strength to Weight: Bending, points | 15 | |
| 9.9 to 18 |
| Thermal Diffusivity, mm2/s | 110 | |
| 73 |
| Thermal Shock Resistance, points | 16 | |
| 8.9 to 22 |
Alloy Composition
| Copper (Cu), % | 99.9 to 100 | |
| 96.5 to 98.6 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0.9 to 1.3 |
| Phosphorus (P), % | 0 | |
| 0.15 to 0.35 |
| Tellurium (Te), % | 0 | |
| 0.35 to 0.6 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |